Charge carrier transport and nanomorphology control for efficient non-fullerene organic solar cells
Fong, Patrick W.K.
KAUST DepartmentPhysical Sciences and Engineering (PSE) Division
Chemical Science Program
KAUST Solar Center (KSC)
Permanent link to this recordhttp://hdl.handle.net/10754/653048
MetadataShow full item record
AbstractSingle junction organic photovoltaic devices (OPVs) have exceeded 15% power conversion efficiency (PCE) with the help of fused ring based low-bandgap non-fullerene acceptors (NFAs). As a major type of NFA, the indacenodithiophene derivative NFA (IDTBR) has been shown to have superior OPV stability with outstanding VOC, but the efficiency is relatively lower compared to the reported OPV champion devices. Further improvements towards high efficiencies in this OPV system remains challenging due to the relatively poor charge carrier transport properties in the bulk heterojunction film, particularly the electron transport in small molecule non-fullerene acceptor network. Here we conducted detailed study on the dependence of carrier transport on BHJ donor–acceptor (D–A) composition. Our results show that the nano-morphology or phase aggregation of non-fullerene acceptor (NFA) molecules can be tuned via D–A composition in bulk heterojunction layer, and the improvement of electron mobility was shown to be enhanced by almost one order – from 1.23 × 10−6 cm2/V (D:A = 1:1 by weight) to 1.02 × 10−5 cm2/V (D:A = 1:2) – due to the improved connectivity of electron transport pathways. Further increase of NFA component content, however, has led to over-sized phase segregation, deteriorating the photovoltaic performance of organic soar cells. The optimized BHJ cell shows more balanced charge carrier transport and phase segregation, which yields a PCE of 10.79%. Furthermore, it shows a VOC as high as 1.03 V, which is ascribed to the significantly suppressed radiative and non-radiative recombination losses with bandgap-VOC offset Eg/q-VOC of only 0.55 V.
CitationHu H, Deng W, Qin M, Yin H, Lau T-K, et al. (2019) Charge carrier transport and nanomorphology control for efficient non-fullerene organic solar cells. Materials Today Energy 12: 398–407. Available: http://dx.doi.org/10.1016/j.mtener.2019.04.005.
SponsorsThis work was supported by Shenzhen Science and Technology Innovation Commission (Project No. JCYJ20170413154602102), Research Grants Council of Hong Kong (Grant No. 15246816, and 15218517), the Project of Strategic Importance provided by the Hong Kong Polytechnic University (Project No. 1-ZE29). W.Z acknowledges financial support from National Natural Science Foundation of China (21464003). X.L thanks Research Grant Council of Hong Kong (General Research Fund No. 14314216). H.W is grateful of National Natural Science Foundation of China (No. 51521002 and 61775061) for the financial support.
JournalMaterials Today Energy