Characterizing the influence of matrix ductility on damage phenomenology in continuous fiber-reinforced thermoplastic laminates undergoing quasi-static indentation
KAUST DepartmentComposite and Heterogeneous Material Analysis and Simulation Laboratory (COHMAS)
Mechanical Engineering Program
Physical Science and Engineering (PSE) Division
Online Publication Date2017-12-12
Print Publication Date2018-02
Permanent link to this recordhttp://hdl.handle.net/10754/626406
MetadataShow full item record
AbstractThe use of thermoplastic matrix was known to improve the impact properties of laminated composites. However, different ductility levels can exist in a single family of thermoplastic matrix, and this may consequently modify the damage phenomenology of thermoplastic composites. This paper focuses on the effect of matrix ductility on the out-of-plane properties of thermoplastic composites, which was studied through quasi-static indentation (QSI) test that may represent impact problem albeit the speed difference. We evaluated continuous glass-fiber reinforced polypropylene thermoplastic composites (GFPP), and selected homopolymer PP and copolymer PP that represent ductile and less ductile matrices, respectively. Several cross-ply laminates were selected to study the influence of ply thicknesses and relative orientation of interfaces on QSI properties of GFPP. It is expected that GFPP with ductile matrix improves energy absorption of GFPP. However, the damage mechanism is completely different between GFPP with ductile and GFPP with less ductile matrices. GFPP with ductile matrix exhibits smaller damage zone in comparison to the one with less ductile matrix. Higher matrix ductility inhibits the growth of ply cracking along the fiber, and this causes the limited size of delamination. The stacking sequence poses more influence on less ductile composites rather than the ductile one.
CitationYudhanto A, Wafai H, Lubineau G, Yaldiz R, Verghese N (2017) Characterizing the influence of matrix ductility on damage phenomenology in continuous fiber-reinforced thermoplastic laminates undergoing quasi-static indentation. Composite Structures. Available: http://dx.doi.org/10.1016/j.compstruct.2017.12.028.
SponsorsThe research reported in this publication was supported by SABIC and by the King Abdullah University of Science and Technology (KAUST). We thank Mr. Warden Schijve (SABIC) and Mr. Ditho Pulungan (COHMAS, KAUST) for the discussion, Mr. Ran Tao (COHMAS, KAUST) for assisting with the dent-depth measurement, Dr. Lutfan Sinatra (Functional Nanomaterial Laboratory, KAUST) for assisting with the burn-off test and Mr. Shiva Goutham (COHMAS, KAUST) for assisting with the tensile tests, Mr. Guillaume Ratouit (SABIC) and Mr. Rob Marrees (SABIC) for assisting with C-scan.