Synthesis and Characterization of the Rubidium Thiophosphate Rb 6 (PS 5 )(P 2 S 10 ) and the Rubidium Silver Thiophosphates Rb 2 AgPS 4 , RbAg 5 (PS 4 ) 2 and Rb 3 Ag 9 (PS 4 ) 4
Type
ArticleKAUST Grant Number
BAS/1/1302-01-01Date
2016-02-17Online Publication Date
2016-02-17Print Publication Date
2016-03Permanent link to this record
http://hdl.handle.net/10754/621523
Metadata
Show full item recordAbstract
The metal thiophosphates Rb2AgPS4 (2), RbAg5(PS4)2 (3), and Rb3Ag9(PS4)4 (4) were synthesized by stoichiometric reactions, whereas Rb6(PS5)(P2S10) (1) was prepared with excess amount of sulfur. The compounds crystallize as follows: 1 monoclinic, P21/c (no. 14), a = 17.0123(7) Å, b = 6.9102(2) Å, c = 23.179(1) Å, β = 94.399(4)°; 2 triclinic, P ¯ (no. 2), a = 6.600(1) Å, b = 6.856(1) Å, c = 10.943(3) Å, α = 95.150(2)°, β = 107.338(2)°, γ = 111.383(2)°; 3 orthorhombic, Pbca (no. 61), a = 12.607(1) Å, b = 12.612(1) Å, c = 17.759(2) Å; 4 orthorhombic, Pbcm (no. 57), a = 6.3481(2) Å, b = 12.5782(4) Å, c = 35.975(1) Å. The crystal structures contain discrete units, chains, and 3D polyanionic frameworks composed of PS4 tetrahedral units arranged and connected in different manner. Compounds 1-3 melt congruently, whereas incongruent melting behavior was observed for compound 4. 1-4 are semiconductors with bandgaps between 2.3 and 2.6 eV and thermally stable up to 450 °C in an inert atmosphere. Copyright © 2016 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.Citation
Alahmari F, Davaasuren B, Khanderi J, Rothenberger A (2016) Synthesis and Characterization of the Rubidium Thiophosphate Rb 6 (PS 5 )(P 2 S 10 ) and the Rubidium Silver Thiophosphates Rb 2 AgPS 4 , RbAg 5 (PS 4 ) 2 and Rb 3 Ag 9 (PS 4 ) 4 . Z anorg allg Chem 642: 361–367. Available: http://dx.doi.org/10.1002/zaac.201500793.Sponsors
This research was supported by King Abdullah University of Science and Technology (KAUST) baseline fund BAS/1/1302-01-01.Publisher
WileyAdditional Links
http://onlinelibrary.wiley.com/doi/10.1002/zaac.201500793/fullae974a485f413a2113503eed53cd6c53
10.1002/zaac.201500793