Triptycene dimethyl-bridgehead dianhydride-based intrinsically microporous hydroxyl-functionalized polyimide for natural gas upgrading
KAUST DepartmentPhysical Sciences and Engineering (PSE) Division
Chemical and Biological Engineering Program
Advanced Membranes and Porous Materials Research Center
Materials Science and Engineering Program
Advanced Membranes and Porous Materials Center (AMPMC)
Permanent link to this recordhttp://hdl.handle.net/10754/617799
MetadataShow full item record
AbstractThe synthesis and gas permeation properties of a high-performance hydroxyl-functionalized PIM-polyimide (TDA1-APAF) prepared from a novel 9,10-dimethyl-2,3,6,7-triptycene tetracarboxylic dianhydride (TDA1) and a commercially available 2,2-bis(3-amino-4-hydroxyphenyl)-hexafluoropropane (APAF) diamine monomer are reported. The microporous polymer had a BET surface area based on nitrogen adsorption of 260 m2 g−1. A freshly prepared sample exhibited excellent gas permeation properties: (i) CO2 permeability of 40 Barrer coupled with a CO2/CH4 selectivity of 55 and (ii) H2 permeability of 94 Barrer with a H2/CH4 selectivity of 129. Physical aging over 250 days resulted in significantly enhanced CO2/CH4 and H2/CH4 selectivities of 75 and 183, respectively with only ~ 25% loss in CO2 and H2 permeability. Aged TDA1-APAF exhibited 5-fold higher pure-gas CO2 permeability (30 Barrer) and two-fold higher CO2/CH4 permselectivity over conventional dense cellulose triacetate membranes at 2 bar. In addition, TDA1-APAF polyimide had a N2/CH4 selectivity of 2.3, thereby making it potentially possible to bring natural gas with low, but unacceptable nitrogen content to pipeline specification. Gas mixture permeation experiments with a 1:1 CO2/CH4 feed mixture demonstrated higher mixed- than pure-gas selectivity and plasticization resistance up to 30 bar. These results suggest that intrinsically microporous hydroxyl-functionalized triptycene-based polyimides are promising candidate membrane materials for removal of CO2 from natural gas and hydrogen purification in petrochemical refinery applications.
CitationTriptycene dimethyl-bridgehead dianhydride-based intrinsically microporous hydroxyl-functionalized polyimide for natural gas upgrading 2016 Journal of Membrane Science
SponsorsThe research reported in this publication was supported by funding from King Abdullah University of Science and Technology (KAUST).
JournalJournal of Membrane Science