Pure- and Mixed-Gas Permeation Properties of Highly Selective and Plasticization Resistant Hydroxyl-Diamine-Based 6FDA Polyimides for CO2/CH4 Separation
KAUST DepartmentAdvanced Membranes and Porous Materials Research Center
Physical Sciences and Engineering (PSE) Division
Chemical and Biological Engineering Program
MetadataShow full item record
AbstractThe effect of hydroxyl functionalization on the m-phenylene diamine moiety of 6FDA dianhydride-based polyimides was investigated for gas separation applications. Pure-gas permeability coefficients of He, H2, N2, O2, CH4, and CO2 were measured at 35 °C and 2 atm. The introduction of hydroxyl groups in the diamine moiety of 6FDA-diaminophenol (DAP) and 6FDA-diamino resorcinol (DAR) polyimides tightened the overall polymer structure due to increased charge transfer complex formation compared to unfunctionalized 6FDA-m-phenylene diamine (mPDA). The BET surface areas based on nitrogen adsorption of 6FDA-DAP (54 m2g−1) and of 6FDA-DAR (45 m2g−1) were ~18% and 32% lower than that of 6FDA-mPDA (66 m2g−1). 6FDA-mPDA had a pure-gas CO2 permeability of 14 Barrer and CO2/CH4 selectivity of 70. The hydroxyl-functionalized polyimides 6FDA-DAP and 6FDA-DAR exhibited very high pure-gas CO2/CH4 selectivities of 92 and 94 with moderate CO2 permeability of 11 and 8 Barrer, respectively. It was demonstrated that hydroxyl-containing polyimide membranes maintained very high CO2/CH4 selectivity (~ 75 at CO2 partial pressure of 10 atm) due to CO2 plasticization resistance when tested under high-pressure mixed-gas conditions. Functionalization with hydroxyl groups may thus be a promising strategy towards attaining highly selective polyimides for economical membrane-based natural gas sweetening.
CitationPure- and Mixed-Gas Permeation Properties of Highly Selective and Plasticization Resistant Hydroxyl-Diamine-Based 6FDA Polyimides for CO2/CH4 Separation 2016 Journal of Membrane Science
JournalJournal of Membrane Science