Physicochemical properties of manganese dioxide synthesized using C2–C5 alcohols as reducing agents and their catalytic activities for CO oxidation
Online Publication Date2015-09-27
Print Publication Date2016-05
Permanent link to this recordhttp://hdl.handle.net/10754/579545
MetadataShow full item record
AbstractMnO2 catalysts were synthesized in an aqueous solution of KMnO4 and C2–C5 alcohols using a simple redox method at room temperature. The crystalline structure of all samples was δ-MnO2 after being calcined at 300 °C. However, other physicochemical properties of the samples varied depending on the symmetry of the alcohols used. For the catalytic oxidation of CO, MnO2 catalysts prepared with 1° alcohols performed better than the samples prepared in 2° alcohols. Catalytic activities were correlated to the quantity of labile oxygen species of the catalysts. In CO-TPD analysis, the relative area of desorbed radical dotCO2, which is the product of the reaction between adsorbed CO and lattice oxygen species, becomes larger for MnO2 prepared with 1° alcohols than with 2° alcohols. These results were primarily resulted from the innate hydrogen dissociation behavior of alcohol in solution. The pKa was found to be an important factor in determining the physicochemical properties and catalytic activity toward CO oxidation of MnO2.
CitationLee, Y.-H., Park, J.-H., & Shin, C.-H. (2016). Physicochemical properties of manganese dioxide synthesized using C2–C5 alcohols as reducing agents and their catalytic activities for CO oxidation. Catalysis Today, 265, 7–13. doi:10.1016/j.cattod.2015.08.032