(La, Pr)0.8Sr0.2FeO3-δ-Sm 0.2Ce0.8O2-δ composite cathode for proton-conducting solid oxide fuel cells
Isimjan, Tayirjan T.
KAUST DepartmentKAUST Solar Center (KSC)
Material Science and Engineering Program
Physical Science and Engineering (PSE) Division
Permanent link to this recordhttp://hdl.handle.net/10754/564968
MetadataShow full item record
AbstractMixed rare-earth (La, Pr)0.8Sr0.2FeO 3-δ-Sm0.2Ce0.8O2-δ (LPSF-SDC) composite cathode was investigated for proton-conducting solid oxide fuel cells based on protonic BaZr0.1Ce0.7Y 0.2O3-δ (BZCY) electrolyte. The powders of La 0.8-xPrxSr0.2FeO3-δ (x = 0, 0.2, 0.4, 0.6), Sm0.2Ce0.8O2-δ (SDC) and BaZr0.1Ce0.7Y0.2O3-δ (BZCY) were synthesized by a citric acid-nitrates self-propagating combustion method. The XRD results indicate that La0.8-xPrxSr 0.2FeO3-δ samples calcined at 950 °C exhibit perovskite structure and there are no interactions between LPSF0.2 and SDC at 1100 °C. The average thermal expansion coefficient (TEC) of LPSF0.2-SDC, BZCY and NiO-BZCY is 12.50 × 10-6 K-1, 13.51 × 10-6 K-1 and 13.47 × 10-6 K -1, respectively, which can provide good thermal compatibility between electrodes and electrolyte. An anode-supported single cell of NiO-BZCY|BZCY|LPSF0.2-SDC was successfully fabricated and operated from 700 °C to 550 °C with humidified hydrogen (∼3% H2O) as fuel and the static air as oxidant. A high maximum power density of 488 mW cm -2, an open-circuit potential of 0.95 V, and a low electrode polarization resistance of 0.071 Ω cm2 were achieved at 700 °C. Preliminary results demonstrate that LPSF0.2-SDC composite is a promising cathode material for proton-conducting solid oxide fuel cells. © 2014, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.
CitationChen, Y., Gu, Q., Tian, D., Ding, Y., Lu, X., Yu, W., … Lin, B. (2014). (La, Pr)0.8Sr0.2FeO3−–Sm0.2Ce0.8O2− composite cathode for proton-conducting solid oxide fuel cells. International Journal of Hydrogen Energy, 39(25), 13665–13670. doi:10.1016/j.ijhydene.2014.04.042
SponsorsThe authors would like to thank the financial support from Chinese Natural Science Foundation on contract Grant (No. 51102107 and No. 51202080), Anhui Science and Technology Project (No. 1206c0805038) and Huainan Science and Technology Project (No. 2010A03203).