Electrical performance of polymer ferroelectric capacitors fabricated on plastic substrate using transparent electrodes
KAUST DepartmentMaterials Science and Engineering Program
Physical Sciences and Engineering (PSE) Division
Functional Nanomaterials and Devices Research Group
Permanent link to this recordhttp://hdl.handle.net/10754/562286
MetadataShow full item record
AbstractPolymer-based flexible ferroelectric capacitors have been fabricated using a transparent conducting oxide (ITO) and a transparent conducting polymer (PEDOT:PSS). It is found that the polarization fatigue performance with transparent oxide electrodes exhibits a significant improvement over the polymer electrodes (20% vs 70% drop in polarization after 10 6 cycles). This result can be explained based on a charge injection model that is controlled by interfacial band-offsets, and subsequent pinning of ferroelectric domain walls by the injected carriers. Furthermore, the coercive field (E c) of devices with our polymer electrodes is nearly 40% lower than reported values with similar polymer electrodes. Surprisingly, this difference was found to be related to the dry etching process used to define the top electrodes, which is reported for the first time by this group. The temperature dependence of relative permittivity of both devices shows a typical first order ferroelectric-to-paraelectric phase transition, but with a reduced Curie temperature compared to reference devices fabricated on Pt. © 2012 Elsevier B.V. All rights reserved.
SponsorsThe authors would like to thank Mr. Ahad Syed (Nano-Fab, KAUST) for his help with optimizing the oxygen plasma dry etch recipe, Dr. Dongkyu Cha and M. Almadhoun for characterization and analysis. The authors also acknowledge the generous financial support from the KAUST baseline fund and Saudi Basic Industries (SABIC) Grant No. 2000000015.