Janjua, Bilal; Ng, Tien Khee; Zhao, Chao; Oubei, Hassan M.; Shen, Chao; Prabaswara, Aditya; Alias, Mohd Sharizal; Alhamoud, Abdullah; Alatawi, Abdullah; Albadri, Abdulrahman M.; Alyamani, Ahmed Y.; El-Desouki, Munir M.; Ooi, Boon S.(Optics Express, The Optical Society, 2016-08-10)[Article]
Group-III-nitride laser diode (LD)-based solid-state lighting device has been demonstrated to be droop-free compared to light-emitting diodes (LEDs), and highly energy-efficient compared to that of the traditional incandescent and fluorescent white light systems. The YAG:Ce3+ phosphor used in LD-based solid-state lighting, however, is associated with rapid degradation issue. An alternate phosphor/LD architecture, which is capable of sustaining high temperature, high power density, while still intensity- and bandwidth-tunable for high color-quality remained unexplored. In this paper, we present for the first time, the proof-of-concept of the generation of high-quality white light using an InGaN-based orange nanowires (NWs) LED grown on silicon, in conjunction with a blue LD, and in place of the compound-phosphor. By changing the relative intensities of the ultrabroad linewidth orange and narrow-linewidth blue components, our LED/LD device architecture achieved correlated color temperature (CCT) ranging from 3000 K to above 6000K with color rendering index (CRI) values reaching 83.1, a value unsurpassed by the YAG-phosphor/blue-LD counterpart. The white-light wireless communications was implemented using the blue LD through on-off keying (OOK) modulation to obtain a data rate of 1.06 Gbps. We therefore achieved the best of both worlds when orange-emitting NWs LED are utilized as “active-phosphor”, while blue LD is used for both color mixing and optical wireless communications.
Shen, Chao; Ng, Tien Khee; Leonard, John T.; Pourhashemi, Arash; Oubei, Hassan M.; Alias, Mohd Sharizal; Nakamura, Shuji; DenBaars, Steven P.; Speck, James S.; Alyamani, Ahmed Y.; Eldesouki, Munir M.; Ooi, Boon S.(ACS Photonics, American Chemical Society (ACS), 2016-02-05)[Article]
To date, solid-state lighting (SSL), visible light communication (VLC) and optical clock generation functionalities in the blue-green color regime have been demonstrated based on discrete devices, including light-emitting diodes, laser diodes, and transverse-transmission modulators. This work presents the first integrated waveguide modulator-laser diode (IWM-LD) at 448 nm, offering the advantages of small-footprint, high-speed, and low power-consumption. A high modulation efficiency of 2.68 dB/V, deriving from a large extinction ratio of 9.4 dB and a low operating voltage range of 3.5 V, was measured. The electroabsorption characteristics revealed that the modulation effect, as observed from the red-shifting of the absorption edge, was resulted from the external-field-induced quantum-confined-Stark-effect (QCSE). A comparative analysis of the photocurrent versus wavelength spectra in semipolar- and polar-plane InGaN/GaN quantum wells (QWs) confirmed that the IWM-LD based on semipolar (20¯2 ¯1) QWs was able to operate in a manner similar to other III-V materials typically used in optical telecommunications, due to the reduced piezoelectric field. Utilizing the integrated modulator, a -3dB bandwidth of ~1 GHz was measured, and a data rate of 1 Gbit/s was demonstrated using on-off keying (OOK) modulation. Our experimental investigation highlighted the advantage of implementing the IWM-LD on the same semipolar QW epitaxy in enabling a high-efficiency platform for SSL-VLC dual-functionalities.
Export search results
The export option will allow you to export the current search results of the entered query to a file. Different
formats are available for download. To export the items, click on the button corresponding with the preferred download format.
By default, clicking on the export buttons will result in a download of the allowed maximum amount of items.
For anonymous users the allowed maximum amount is 50 search results.
To select a subset of the search results, click "Selective Export" button and make a selection of the items you want to export.
The amount of items that can be exported at once is similarly restricted as the full export.
After making a selection, click one of the export format buttons. The amount of items that will be exported is indicated in the bubble next to export format.