Effect of heat, UV radiation, and moisture on the decohesion kinetics of inverted organic solar cells

Handle URI:
http://hdl.handle.net/10754/625117
Title:
Effect of heat, UV radiation, and moisture on the decohesion kinetics of inverted organic solar cells
Authors:
Rolston, Nicholas; Printz, Adam D.; Dupont, Stephanie R.; Voroshazi, Eszter; Dauskardt, Reinhold H.
Abstract:
Organic solar cells subjected to environmental stressors such as heat, moisture, and UV radiation can undergo significant mechanical degradation, leading to delamination of layers and device failure. This paper reports the effect these stressors have on the mechanical integrity of active layers and interfaces as measured by subcritical debonding tests, and the in situ evolution of defects and fracture processes is characterized. At elevated temperatures below 50 °C in inert conditions, significant device weakening was observed, an effect we attributed to a temperature-induced P3HT:PCBM delamination mechanism from the underlying ZnO. At 50 °C in ambient conditions with UV exposure—selected to better simulate real-world environments—devices were more resistant to fracture because of an interfacial strengthening effect from increased hydrogen bonding where UV-induced Zn(OH)2 formation reinforced the interface with P3HT:PCBM. This photoinduced hydroxylation mechanism was determined from a decrease in the Zn/O ratio with increased UVA or UVB exposure, and hydroxylation was shown to directly correlate with the resistance to fracture in devices.
Citation:
Rolston N, Printz AD, Dupont SR, Voroshazi E, Dauskardt RH (2017) Effect of heat, UV radiation, and moisture on the decohesion kinetics of inverted organic solar cells. Solar Energy Materials and Solar Cells 170: 239–245. Available: http://dx.doi.org/10.1016/j.solmat.2017.06.002.
Publisher:
Elsevier BV
Journal:
Solar Energy Materials and Solar Cells
KAUST Grant Number:
KUS-C1-015-21
Issue Date:
15-Jun-2017
DOI:
10.1016/j.solmat.2017.06.002
Type:
Article
ISSN:
0927-0248
Sponsors:
This research was supported by the Center for Advanced Molecular Photovoltaics (CAMP) supported by King Abdullah University of Science and Technology (KAUST) under award no. KUS-C1-015-21. Additional support was provided by the National Science Foundation Graduate Research Fellowship, awarded to N. Rolston under award no. DGE-1656518. Part of this work was performed at the Stanford Nano Shared Facilities (SNSF), supported by the National Science Foundation under award ECCS-1542152.
Appears in Collections:
Publications Acknowledging KAUST Support

Full metadata record

DC FieldValue Language
dc.contributor.authorRolston, Nicholasen
dc.contributor.authorPrintz, Adam D.en
dc.contributor.authorDupont, Stephanie R.en
dc.contributor.authorVoroshazi, Eszteren
dc.contributor.authorDauskardt, Reinhold H.en
dc.date.accessioned2017-06-21T06:51:52Z-
dc.date.available2017-06-21T06:51:52Z-
dc.date.issued2017-06-15en
dc.identifier.citationRolston N, Printz AD, Dupont SR, Voroshazi E, Dauskardt RH (2017) Effect of heat, UV radiation, and moisture on the decohesion kinetics of inverted organic solar cells. Solar Energy Materials and Solar Cells 170: 239–245. Available: http://dx.doi.org/10.1016/j.solmat.2017.06.002.en
dc.identifier.issn0927-0248en
dc.identifier.doi10.1016/j.solmat.2017.06.002en
dc.identifier.urihttp://hdl.handle.net/10754/625117-
dc.description.abstractOrganic solar cells subjected to environmental stressors such as heat, moisture, and UV radiation can undergo significant mechanical degradation, leading to delamination of layers and device failure. This paper reports the effect these stressors have on the mechanical integrity of active layers and interfaces as measured by subcritical debonding tests, and the in situ evolution of defects and fracture processes is characterized. At elevated temperatures below 50 °C in inert conditions, significant device weakening was observed, an effect we attributed to a temperature-induced P3HT:PCBM delamination mechanism from the underlying ZnO. At 50 °C in ambient conditions with UV exposure—selected to better simulate real-world environments—devices were more resistant to fracture because of an interfacial strengthening effect from increased hydrogen bonding where UV-induced Zn(OH)2 formation reinforced the interface with P3HT:PCBM. This photoinduced hydroxylation mechanism was determined from a decrease in the Zn/O ratio with increased UVA or UVB exposure, and hydroxylation was shown to directly correlate with the resistance to fracture in devices.en
dc.description.sponsorshipThis research was supported by the Center for Advanced Molecular Photovoltaics (CAMP) supported by King Abdullah University of Science and Technology (KAUST) under award no. KUS-C1-015-21. Additional support was provided by the National Science Foundation Graduate Research Fellowship, awarded to N. Rolston under award no. DGE-1656518. Part of this work was performed at the Stanford Nano Shared Facilities (SNSF), supported by the National Science Foundation under award ECCS-1542152.en
dc.publisherElsevier BVen
dc.subjectDecohesion kineticsen
dc.subjectReliabilityen
dc.subjectHydroxylationen
dc.subjectOrganic photovoltaicsen
dc.titleEffect of heat, UV radiation, and moisture on the decohesion kinetics of inverted organic solar cellsen
dc.typeArticleen
dc.identifier.journalSolar Energy Materials and Solar Cellsen
dc.contributor.institutionDepartment of Applied Physics, Stanford University, Stanford, CA, USAen
dc.contributor.institutionDepartment of Materials Science and Engineering, Stanford University, Stanford, CA, USAen
dc.contributor.institutionIMEC vzw, Leuven, Belgiumen
kaust.grant.numberKUS-C1-015-21en
All Items in KAUST are protected by copyright, with all rights reserved, unless otherwise indicated.