Efficient Transfer of Graphene-Physical and Electrical Performance Perspective

Handle URI:
http://hdl.handle.net/10754/253733
Title:
Efficient Transfer of Graphene-Physical and Electrical Performance Perspective
Authors:
Ghoneim, Mohamed T. ( 0000-0002-5568-5284 )
Abstract:
Efficient Transfer of Graphene –Physical and Electrical Performance Perspective Graphene has become one of the most widely used atomic crystal structure materials since its first experimental proof by Geim-Novoselov in 2004 [1]. This is attributed to its reported incredible carrier mobility, mechanical strength and thermal conductivity [2] [3] [4]. These properties suggest interesting applications of Graphene ranging from electronics to energy storage and conversion [5]. In 2008, Chen et al reported a 40,000 cm2V-1s-1 mobility for a Single Layer Graphene (SLG) on SiO2 compared to 285 cm2V-1s-1 for silicon channel devices [6]. Chemical vapor deposition (CVD) is a common method for growing graphene on a metal surface as a catalyst for graphene nucleation. This adds a necessary transfer step to the target substrate ultimately desired for graphene devices fabrication. Interfacing with graphene is a critical challenge in preserving its promising high mobility. This initiated the motivation for studying the effect of intermediate interfaces imposed by transfer processes. In this work, few layers graphene (FLG) was grown on copper foils inside a high temperature furnace. Then Raman spectroscopy was performed on grown graphene sample to confirm few (in between 3-10) layers. Afterwards the sample was cut into three pieces and transferred to 300 nm SiO2 on Si substrates using three techniques, namely: (i) pickup transfer with top side of Graphene brought in contact with SiO2 [7], (ii) Ploy (methyl methacrylate) (PMMA) transfer with Graphene and a PMMA support layer on top scooped from bottom side [8], and (iii) a modified direct transfer which is similar to PMMA transfer without the support layer [9]. Comparisons were done using Raman spectroscopy to determine the relative defectivity, Scanning Electron Microscopy (SEM) to observe discontinuities and Atomic Force Microscopy (AFM) to measure surface roughness. Then we conclude with electrical data based on the contact resistivity measured for layers transferred using these different techniques. Contacts were deposited using e-beam thermal evaporation and contact resistivity was calculated using Transmission Line Method (TLM) [10]. To date no comparative analysis for the aforementioned transfer methods has been done to determine which is the most efficient [5]. Our contributions are: (i) determining the most efficient method, (ii) reporting a lift-off process for Graphene, (ii) and reporting lower specific contact resistivity for no-post transfer processing Graphene.
Advisors:
Hussain, Muhammad Mustafa ( 0000-0003-3279-0441 )
Committee Member:
Lai, Zhiping ( 0000-0001-9555-6009 ) ; Shamim, Atif ( 0000-0002-4207-4740 )
KAUST Department:
Computer, Electrical and Mathematical Sciences and Engineering (CEMSE) Division
Program:
Electrical Engineering
Issue Date:
Nov-2012
Type:
Thesis
Appears in Collections:
Theses; Electrical Engineering Program; Computer, Electrical and Mathematical Sciences and Engineering (CEMSE) Division

Full metadata record

DC FieldValue Language
dc.contributor.advisorHussain, Muhammad Mustafaen
dc.contributor.authorGhoneim, Mohamed T.en
dc.date.accessioned2012-11-28T14:29:08Z-
dc.date.available2012-11-28T14:29:08Z-
dc.date.issued2012-11en
dc.identifier.urihttp://hdl.handle.net/10754/253733en
dc.description.abstractEfficient Transfer of Graphene –Physical and Electrical Performance Perspective Graphene has become one of the most widely used atomic crystal structure materials since its first experimental proof by Geim-Novoselov in 2004 [1]. This is attributed to its reported incredible carrier mobility, mechanical strength and thermal conductivity [2] [3] [4]. These properties suggest interesting applications of Graphene ranging from electronics to energy storage and conversion [5]. In 2008, Chen et al reported a 40,000 cm2V-1s-1 mobility for a Single Layer Graphene (SLG) on SiO2 compared to 285 cm2V-1s-1 for silicon channel devices [6]. Chemical vapor deposition (CVD) is a common method for growing graphene on a metal surface as a catalyst for graphene nucleation. This adds a necessary transfer step to the target substrate ultimately desired for graphene devices fabrication. Interfacing with graphene is a critical challenge in preserving its promising high mobility. This initiated the motivation for studying the effect of intermediate interfaces imposed by transfer processes. In this work, few layers graphene (FLG) was grown on copper foils inside a high temperature furnace. Then Raman spectroscopy was performed on grown graphene sample to confirm few (in between 3-10) layers. Afterwards the sample was cut into three pieces and transferred to 300 nm SiO2 on Si substrates using three techniques, namely: (i) pickup transfer with top side of Graphene brought in contact with SiO2 [7], (ii) Ploy (methyl methacrylate) (PMMA) transfer with Graphene and a PMMA support layer on top scooped from bottom side [8], and (iii) a modified direct transfer which is similar to PMMA transfer without the support layer [9]. Comparisons were done using Raman spectroscopy to determine the relative defectivity, Scanning Electron Microscopy (SEM) to observe discontinuities and Atomic Force Microscopy (AFM) to measure surface roughness. Then we conclude with electrical data based on the contact resistivity measured for layers transferred using these different techniques. Contacts were deposited using e-beam thermal evaporation and contact resistivity was calculated using Transmission Line Method (TLM) [10]. To date no comparative analysis for the aforementioned transfer methods has been done to determine which is the most efficient [5]. Our contributions are: (i) determining the most efficient method, (ii) reporting a lift-off process for Graphene, (ii) and reporting lower specific contact resistivity for no-post transfer processing Graphene.en
dc.language.isoenen
dc.subjectGrapheneen
dc.subjectperformanceen
dc.titleEfficient Transfer of Graphene-Physical and Electrical Performance Perspectiveen
dc.typeThesisen
dc.contributor.departmentComputer, Electrical and Mathematical Sciences and Engineering (CEMSE) Divisionen
thesis.degree.grantorKing Abdullah University of Science and Technologyen_GB
dc.contributor.committeememberLai, Zhipingen
dc.contributor.committeememberShamim, Atifen
thesis.degree.disciplineElectrical Engineeringen
thesis.degree.nameMaster of Scienceen
dc.person.id117936en
All Items in KAUST are protected by copyright, with all rights reserved, unless otherwise indicated.